    Titanium Anodizing ???'s

    Mike ( Bosox06 ), how did you obtain getting your Ti skids anodized Black??

    You told me you let them soak for a long time to achieve this. What voltage did you use then to get them to this color?? This I need to know please!

    All Titanium reaches a specific color depending on what voltage is used in the solution for the part. I have spoke with several Titanium anodizing experts and all of them say it must be a Titanium Nitride coating instead of anodizing because it is impossible to achieve a " shade " like Black because Black is not a color and Titanium anodizing only produces color.

    So in all I am getting a lot of mixed information on this but you have achieved it so could you please give the specifics on how you did this since you did it yourself??

    It is greatly appreciated! Thanks!

  2. #2
    RCMTC-MI MiRatlhed's Avatar
    Join Date
    Apr 2009
    Location
    Gibsonton, FL
    Posts
    1,890
    By any chance did you use a nitrate electrolyte and black dye solution??

  3. #3
    RCMTC-MI MiRatlhed's Avatar
    Join Date
    Apr 2009
    Location
    Gibsonton, FL
    Posts
    1,890
    MODS CAN DELETE THIS THREAD, THANKS!

  4. #4
    if it aint broke,ur not pushn it
    Join Date
    Jul 2012
    Location
    crofton md
    Posts
    218
    i say keep this! lol its useful
    stock=broken...if its stock thats cuz im trying to break it to build it better

  5. #5
    RCMTC-MI MiRatlhed's Avatar
    Join Date
    Apr 2009
    Location
    Gibsonton, FL
    Posts
    1,890
    I found that black is indeed a coating. Pretty costly process unless you intend to do multiple parts.

  6. #6
    if it aint broke,ur not pushn it
    Join Date
    Jul 2012
    Location
    crofton md
    Posts
    218
    I think doing multiple parts for multiple builds is the way to go!...ive been thinkn its time for more unique builds
    stock=broken...if its stock thats cuz im trying to break it to build it better

Thread Information

Users Browsing this Thread

There are currently 1 users browsing this thread. (0 members and 1 guests)

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •